201k2- Self-crosslinking Silane-XLPE Compound for Wires and Cables

Short Description:

Self-crosslinking Silane-XLPE Compound is a type of fast cross linking compound. It is recommended to be used for low-voltage (up to 10kV) wires and cables and has following advantages: good electrical insulation properties, anti-aging properties and tensile strength; the highest continuous working temperature is 90℃, excellent low-temperature brittleness properties.


  • Min.Order Quantity: Up to request
  • Port: Main Port of China
  • Payment Terms: L/C,D/A,D/P,T/T,WU,PAYPAL,TRADE ASSURANCE
  • Packing: Drum, IBC, BAG or As Per Request
  • model number: lby-SCS001
  • Dielectric strength: 38MV/m
  • Color: blue, white, gray, red
  • Tensile strength: ≥20Mpa
  • Certificate: REACH ROHS
  • Elongation: ≥500%
  • Density: 0.92g/cm3
  • MIF(190℃,5.0kg: 4.0g/10min
  • Product Detail

    Product Tags

    No.
    Experiment item
    Test Method
    Unit
    Typical value
    1
    Density
    ASTMD1505
    g/cm3
    0.92
    2
    MFI(190℃,5.0kg)
    ISO1133
    g/10min
    4.0
    3
    Tensile strength
    IEC60811-1-1
    MPa
    20
    4
    Elongation at break
    IEC60811-1-1
    500
    5
    Brittleness temperature
    -76℃、30pieces
    0
    Pieces
    0
    6
    Change of tensile strength Change of elongation at break
    after aging 135±2℃、168h
    IEC60811-1-2

    +5

    -3

    7
    Hotset 200℃,0.2MPa, 15min Elongation rate under load Permanent deformation after cooling
    IEC60811-2-1

    50

    0

    8
    DC Volume resistivity 20 ℃
    IEC 60093-1980
    Ω.m
    1×10^14
    9
    Dielectric strength
    IEC 60243-1-1988
    MV/m
    38