201k2- Self-crosslinking Silane-XLPE Compound for Wires and Cables
No.
|
Experiment item
|
Test Method
|
Unit
|
Typical value
|
1
|
Density
|
ASTMD1505
|
g/cm3
|
0.92
|
2
|
MFI(190℃,5.0kg)
|
ISO1133
|
g/10min
|
4.0
|
3
|
Tensile strength
|
IEC60811-1-1
|
MPa
|
20
|
4
|
Elongation at break
|
IEC60811-1-1
|
%
|
500
|
5
|
Brittleness temperature
-76℃、30pieces |
0
|
Pieces
|
0
|
6
|
Change of tensile strength Change of elongation at break
after aging 135±2℃、168h |
IEC60811-1-2
|
%
% |
+5
-3 |
7
|
Hotset 200℃,0.2MPa, 15min Elongation rate under load Permanent deformation after cooling
|
IEC60811-2-1
|
%
% |
50
0 |
8
|
DC Volume resistivity 20 ℃
|
IEC 60093-1980
|
Ω.m
|
1×10^14
|
9
|
Dielectric strength
|
IEC 60243-1-1988
|
MV/m
|
38
|